Home ProductsAlumina Silicate Refractory Brick

High Temperature Castable Fire Brick , Aluminum Silicate Refractory Brick

High Temperature Castable Fire Brick , Aluminum Silicate Refractory Brick

    • High Temperature Castable Fire Brick , Aluminum Silicate Refractory Brick
    • High Temperature Castable Fire Brick , Aluminum Silicate Refractory Brick
    • High Temperature Castable Fire Brick , Aluminum Silicate Refractory Brick
  • High Temperature Castable Fire Brick , Aluminum Silicate Refractory Brick

    Product Details:

    Place of Origin: China
    Brand Name: Jansincere
    Certification: ISO9001, ISO14001
    Model Number: ASR-003

    Payment & Shipping Terms:

    Minimum Order Quantity: 5 tons
    Price: $350-1000$ per ton
    Packaging Details: Wooden pallet
    Delivery Time: 30-45 days after received the deposit
    Payment Terms: L/C, D/A, D/P, T/T, Western Union
    Supply Ability: 2000 tons per year
    Contact Now
    Detailed Product Description
    Al2O3: ≥45% Apparent Porosity: ≤22%
    Bulk Density: 2.65-2.85 G/cm³ Compress Strength, Mpa: ≥60
    Creep Rate: ≤0.8 Mpa Permanent Linear Change: 0.1-0.2%
    Product Name: Aluminum Silicate Brick Type: Brick
    Feature: High Temperature Resistance
    High Light:

    lightweight fire brick

    ,

    low duty firebrick

    Pouring System Used High Refractoriness DRL Type High Alumina Brick

    Technical Index:

    Item SK32 SK34 SK36 SK38 High Refractoriness Alumina Refractory Brick
    DRL-155 DRL-150 DRL-145 DRL-140 DRL-135 DRL-130 DRL-127
    Al2O3,% ≥ 75 75 65 65 65 60 50
    Apparent Porosity,% ≤ 20 21 21 22 22 22 23
    Bulk Density, g/cm3 2.65-2.85 2.65-2.85 2.50-2.70 2.40-2.60 2.35-2.30 2.30-2.50 2.30-2.50
    Compress Strength, Mpa ≥ 60 60 60 55 55 55 50
    Creep Rate, %
    (0.2Mpa,50h) ≤
    1550℃
    0.8
    1500℃
    0.8
    1450℃
    0.8
    1400℃
    0.8
    1350℃
    0.8
    1300℃
    0.8
    1270℃
    0.8
    Permanent Linear Change % 1550℃,2h 0.1-0.2 0.1-0.2 0.1-0.2 -- -- -- --
    1450℃,2h -- -- -- 0.1-0.2 0.1-0.4 0.1-0.4 0.1-0.4
     

    Characteristics:

    High alumina bricks has Al2O3 content ≥40%, its features are as below:

    • High refractoriness under load.
    • The RUL is higher than fireclay brick as the high content of Al2O3
    • Excellent slag resistance
    • All shapes can be customized according to request

    Usage:

    Alumina bricks are widely used in all high temperature industries, hot blast stove, hot furnace, coke ovens, pizza ovens, CDQ, rotary kilns, cement kilns, incinerators, secondary burning chamber, baking furnace etc.

    High Temperature Castable Fire Brick , Aluminum Silicate Refractory Brick

     

    1. Raw material to factory→checkout→burdening→stirring→mixing→taking out the raw material,
    2)Crushing→Mixing→Shaping→Drying→Firing→Inspection→Packaging and Shipment.
    2.Quality Assurance
    1)Going out the furnace→checkout→packing→qualified product→putting in storage→sale,
    2)The process from raw to product are strictly tested by equipment.
     

     Brick Size or Shapes:

    The shape can be customized according to the brick drawings.

    Brick Size (mm)
    Straight Shape Side Arch

    230*114*65

    250*123*65

    171*113*65

    230*114*20

    230*114*30

    230*114*40

    230*57*65

    520*230*113

    650*230*113

    780*230*113

    452*230*65

    230*150*75

    345*150*75

    230*65/55*114
    230*65/45*114
    230*65/55*171
    230*65/45*171
    230*114*65/55
    230*114*65/45
    230*150/120*75
    230*150/110*75

    Contact Details
    Zhengzhou Jansincere Refractory Co., Ltd

    Contact Person: venus

    Send your inquiry directly to us (0 / 3000)

    Zhengzhou Jansincere Refractory Co., Ltd
    Songlou street
    Tel:86-371-55668168
    Mobile Site Privacy Policy China Good Quality Furnace Refractory Bricks Supplier. © 2018 - 2021 furnacerefractorybricks.com. All Rights Reserved.