Kiln Furnace High Alumina Refractory Bricks High Working Temperature Abrasion Resistance

Kiln Furnace High Alumina Refractory Bricks High Working Temperature Abrasion Resistance

Kiln Furnace High Alumina Refractory Bricks High Working Temperature Abrasion Resistance

Product Details:

Place of Origin: China
Brand Name: Jansincere
Certification: ISO9001, ISO14001
Model Number: HAR-013

Payment & Shipping Terms:

Minimum Order Quantity: 5 tons
Price: $350-1000$ per ton
Packaging Details: Wooden pallet
Delivery Time: 30-45 days after received the deposit
Payment Terms: L/C, D/A, D/P, T/T, Western Union
Supply Ability: 2000 tons per year
Contact Now
Detailed Product Description
Al2O3: ≥45% Apparent Porosity: ≤22%
Bulk Density: 2.65-2.85 G/cm³ Compress Strength, Mpa: ≥60
Creep Rate: ≤0.8 Mpa Permanent Linear Change: 0.1-0.2%
Product Name: Alumina Bricks Feature: Good Abrasion Resistance
Application: Kiln Furnace Certificate: ISO9001
High Light:

high alumina fire bricks

,

fire rated bricks

Alumina Bricks Manufacturer Good Abrasion Resistance High Alumina Anchor Brick for Cement Kiln

Introduction of high alumina brick:
The high alumina bricks comprise of a blend of alumina and ferrous content and their apparent porosity is 15 to 23%. High alumina brick has the feature of high refractoriness and can sustain themselves easily even in high temperature.
 
Application:
High alumina brick is widely used for widely used in blast furnaces, hot bast stove,steel ladle lining, reheating furnace, cement kiln, tunnel kiln,boiler, coke oven, carbon furnace,glass kiln , steel smelting furnace and various kiln lining and thermotechnical equipment, etc.
 
Technical Index:

Item SK32 SK34 SK36 SK38 High Refractoriness Alumina Refractory Brick
DRL-155 DRL-150 DRL-145 DRL-140 DRL-135 DRL-130 DRL-127
Al2O3,% ≥ 75 75 65 65 65 60 50
Apparent Porosity,% ≤ 20 21 21 22 22 22 23
Bulk Density, g/cm3 2.65-2.85 2.65-2.85 2.50-2.70 2.40-2.60 2.35-2.30 2.30-2.50 2.30-2.50
Compress Strength, Mpa ≥ 60 60 60 55 55 55 50
Creep Rate, %
(0.2Mpa,50h) ≤
1550℃
0.8
1500℃
0.8
1450℃
0.8
1400℃
0.8
1350℃
0.8
1300℃
0.8
1270℃
0.8
Permanent Linear Change % 1550℃,2h 0.1-0.2 0.1-0.2 0.1-0.2 -- -- -- --
1450℃,2h -- -- -- 0.1-0.2 0.1-0.4 0.1-0.4 0.1-0.4
 

 

Production process:

Raw material mixing, molding, sintering, selection, packing, delivery.

1) Generally, High Alumina brick was molded by dry pressing.

2) By means of mixing the material uniformity in proportion and ageing mixture some time. Then, pour some powders into the mold and dry pressing.

3) After dry pressing, the adobe needs to be pushed in the drying kiln to stove or stay in the air to dry. This progress will need about 3-5 days.

4) After this progress, then push the adobe into the tunnel furnace or shuttle kiln to burn around 1300C. This progress will be need about 5-7 days.

5) After burning, the finished high alumina brick will be packed on pallet.

Contact Details
Zhengzhou Jansincere Refractory Co., Ltd

Contact Person: venus

Send your inquiry directly to us (0 / 3000)

Zhengzhou Jansincere Refractory Co., Ltd
Songlou street
Tel:86-371-55668168
Mobile Site Privacy Policy China Good Quality Furnace Refractory Bricks Supplier. © 2018 - 2021 furnacerefractorybricks.com. All Rights Reserved.