Superior Penetration Resistance Alkali Resistant Refractory Bricks for Cement Kiln

$Superior Penetration Resistance Alkali Resistant Refractory Bricks for Cement Kiln$
$Superior Penetration Resistance Alkali Resistant Refractory Bricks for Cement Kiln$

$Superior Penetration Resistance Alkali Resistant Refractory Bricks for Cement Kiln$

Product Details:

Place of Origin:	Xinmi City, Henan, China
Brand Name:	Jansincere
Certification:	ISO9001
Model Number:	FRB-026

Payment & Shipping Terms:

Minimum Order Quantity:	5 tons
Price:	US$150.00-US$ 360 per ton and negotiable
Packaging Details:	Wooden pallet, plastic shrink film, paper corner protection and straps protected outside. Pallet size: 9595cm, 100100cm or as request.
Delivery Time:	30-45 days
Payment Terms:	L/C, T/T, Western Union
Supply Ability:	45000 ton of silicon mullite bricks per year

Contact Now

Detailed Product Description

Al2O3:	25-40%	SiO2:	65-70%
Volume Density:	≥2.20g/cm3	Cold Crushing Strength:	≥60MPa
Size:	Standard Size	Application:	Furnace Kiln
High Light:	fire resistant bricks , blast furnace brick

Superior Penetration Resistance Alkali Resistant Refractory Bricks for Cement Kiln

Introduction:

Anti-alkali brick is made of silica, flint clay, combing with other additives reacting with alkaline oxide and efficiently stopping the alkaline slags into the bricks, to achieve the alkali resistance.

Feature:

Bulk density stability
Good anti-erosion character
Superior penetration resistance.
Good slag resistant

Application:

Alkali-resisting bricks are widely used in the cement kilns, such as the areas of preheater, precalciner, and tertiary air duct elbow, ect. The demand amount can be max 30~40% during constructing these areas of kilns.

Index:

Item		High Stength Alkali-Resistant Brick
Chemical Composition(%)	Al₂O₃	25—40
	SiO₂	65-70
	Fe₂O₃	≤2.0
Refractoriness(℃)		≥1650
Volume Density(g/cm³)		≥2.20
Apparent Porosity(%)		≤20
Cold Crushing Strength(MPa)		≥60
Refractoriness Under Load (0.2MPa T0.6,℃)		≥1300
Thermal Conductivity Coefficient (w/m.k)		≤1.28
Thermal shock resistance,Cycles(1100℃,Water-cooling)		≥20

$Superior Penetration Resistance Alkali Resistant Refractory Bricks for Cement Kiln$

Tag:

fire resistant bricks,

blast furnace brick

Contact Details

Zhengzhou Jansincere Refractory Co., Ltd

Contact Person: venus

Other Products

$Standard Size Furnace Refractory Bricks Al2O3 73% Phosphate Thermal Conductivity$
Standard Size Furnace Refractory Bricks Al2O3 73% Phosphate Thermal Conductivity

Product Name: Furnace Refractory Bricks
Refractoriness Under Load: ≥1480℃
Bulk Density: ≥2.75g/cm3
Apparent Porosity: ≤18%

$Heat Proof Furnace Refractory Bricks High Strength Erosion Resistance For Rotary Kiln$
Heat Proof Furnace Refractory Bricks High Strength Erosion Resistance For Rotary Kiln

Product Name: Heat Proof Furnace Bricks
Refractoriness Under Load: ≥1480℃
Bulk Density: ≥2.75g/cm3
Apparent Porosity: ≤18%

$Dense Density High Temp Fire Brick , Cement Kiln Refractory Bricks Alkali Resistant$
Dense Density High Temp Fire Brick , Cement Kiln Refractory Bricks Alkali Resistant

Product Name: Alkali-resistant Brick
Al2O3: 25-40%
SiO2: 65-70%
Fe2O3: ≤2%

$Crystalline Quartz Silica Furnace Refractory Bricks For Hot Blast Stove$
Crystalline Quartz Silica Furnace Refractory Bricks For Hot Blast Stove

Al2O3: ≤1.0%
SiO2: ≥95%
Fe2O3: ≤1%
Maximum Service Temperature: 1700

$Insulation Lightweight Fire Brick , Good Heat Storage High Alumina Refractory Bricks$
Insulation Lightweight Fire Brick , Good Heat Storage High Alumina Refractory Bricks

Al2O3: ≥90%
SiO2: ≤8%
Fe2O3: ≤0.2%
Maximum Service Temperature: 1700

$Phosphate Rotary Kiln Fire Bricks , Erosion Resistance Refractory Fire Bricks$
Phosphate Rotary Kiln Fire Bricks , Erosion Resistance Refractory Fire Bricks

Product Name: Fire Bricks
Refractoriness Under Load: ≥1480℃
Bulk Density: ≥2.75g/cm3
Apparent Porosity: ≤18%

$Thermal Furnace Refractory Bricks Phosphate Refractory Blocks For Rotary Kiln$
Thermal Furnace Refractory Bricks Phosphate Refractory Blocks For Rotary Kiln

Product Name: Special Phosphate Brick
Refractoriness Under Load: ≥1480℃
Bulk Density: ≥2.75g/cm3
Apparent Porosity: ≤18%