Kiln Furnace Mullite Refractory Bricks Low Thermal Conductivity Abrasion Resistance

Kiln Furnace Mullite Refractory Bricks Low Thermal Conductivity Abrasion Resistance

Kiln Furnace Mullite Refractory Bricks Low Thermal Conductivity Abrasion Resistance

Product Details:

Place of Origin: Xinmi city, Henan, China
Brand Name: Jansincere
Certification: ISO 14001, ISO9001, CE
Model Number: MRB-003

Payment & Shipping Terms:

Minimum Order Quantity: 1 ton
Price: $1400.00-1550.00 per ton and can be negotiable
Packaging Details: Wooden pallet, plastic shrink film, paper corner protection and straps protected outside. Pallet size: 95*95cm, 100*100cm or as request.
Delivery Time: 35-40 days after received deposit
Payment Terms: L/C, D/P, T/T, Western Union
Supply Ability: 55000 ton per year
Contact Now
Detailed Product Description
Product Name: Sintered Brick Product Type: Brick Shape
SiO2 %: ≤18 Al2O3 %: ≥80
Bulk Density G/cm3: ≥2.8 Apparent Porosity %: 18
Crushing Strength (MPa): ≥90 Refractoriness Under Load(℃): ≥1650
Thermal Shock Resistance: ≥25 Times Feature: Low Thermal Conductivity
Application: Kiln Furnace

Low Thermal Conductivity Corundum Mullite Compounding Brick for Cement Kiln

Product Introduction:

The heavy part is made with fused mullite, fused corundum and white clay, and the light weight part is made with mullite hollow ball, cyanite, flint clay and white clay, shaped in high pressure, sintered in high temperature.

 

Feature:

High temperature resistance

Good abrasion resistance

Good thermal shock resistance

Good erosion resistance

Llow thermal conductivity

 

Technical Index:

Item Corundum Mullite Compounding Brick
Heavy Light weight
Chemical content % Al2O3 ≥80 ≥35
SiO2 ≤18 50~55
Cr2O3 / /
ZrO2 / /
Fe2O3 ≤0.8 /
Apparent Porosity % ≤18 /
Crushing Strength MPa ≥90 ≥30
RUL ℃ ≥1650 ≥1350
Thermal Shock Resistance 1100℃ ≥25 /
Bulk Density g/cm³ ≥2.8 ≤2.0

Thermal Conductivity ,w/m.k

(600℃±25℃)

2.0 1.0
Refracoriness (℃) ≥1790 ≥1730
Linear Change on Reheating(1350x3h,%) ±0.1 ±0.1

Kiln Furnace Mullite Refractory Bricks Low Thermal Conductivity Abrasion Resistance

 

Manufacturing Process Flow:

First, qualified raw materials enter to our raw materials warehouse

Second, all materials including fine powders, aggregates, binding agent are batched according to the technical agreement.

Third, finished raw materials is shaped by 630 tons pressure machine or 2500 tons automatic hydraulic pressure machine.

Forth, green bricks is dried in the dry kilns between 40℃ and 120 ℃, and then sintering in high temperature according to the firing curve.

Last, check the quality of finished refractory bricks and qualified products are packed as request.