|Place of Origin:||Xinmi city, Henan, China|
|Certification:||ISO 14001, ISO9001, CE|
|Minimum Order Quantity:||1 ton|
|Price:||$1400.00-1550.00 per ton and can be negotiable|
|Packaging Details:||Wooden pallet, plastic shrink film, paper corner protection and straps protected outside. Pallet size: 95*95cm, 100*100cm or as request.|
|Delivery Time:||35-40 days after received deposit|
|Payment Terms:||L/C, D/P, T/T, Western Union|
|Supply Ability:||55000 ton per year|
|Product Name:||Corundum Mullite Compounding Brick||Product Type:||Brick Shape|
|SiO2 %:||≤18||Al2O3 %:||≥80|
|Bulk Density G/cm3:||≥2.8||Apparent Porosity %:||18|
|Crushing Strength (MPa):||≥90||Refractoriness Under Load（℃):||≥1650|
|Thermal Shock Resistance:||≥25 Times|
The light weight part of corundum mullite compounding brick is made with mullite hollow ball, cyanite, flint clay and white clay, shaped in high pressure, sintered in high temperature. It can extend the service life for 3-5 monthes.
Corundum mullite compounding brick is widely used for the lining of rotary kiln and high temperature equipment.
|Item||Corundum Mullite Compounding Brick|
|Chemical content %||Al2O3||≥80||≥35|
|Apparent Porosity %||≤18||/|
|Crushing Strength MPa||≥90||≥30|
|Thermal Shock Resistance 1100℃||≥25||/|
|Bulk Density g/cm³||≥2.8||≤2.0|
Thermal Conductivity ,w/m.k
|Linear Change on Reheating(1350x3h,%)||±0.1||±0.1|
Manufacturing Process Flow:
First, qualified raw materials enter to our raw materials warehouse
Second, all materials including fine powders, aggregates, binding agent are batched according to the technical agreement.
Third, finished raw materials is shaped by 630 tons pressure machine or 2500 tons automatic hydraulic pressure machine.
Forth, green bricks is dried in the dry kilns between 40℃ and 120 ℃, and then sintering in high temperature according to the firing curve.
Last, check the quality of finished refractory bricks and qualified products are packed as request.
Contact Person: venus